test Browse by Author Names Browse by Titles of Works Browse by Subjects of Works Browse by Issue Dates of Works
       

Advanced Search
Home   
 
Browse   
Communities
& Collections
  
Issue Date   
Author   
Title   
Subject   
 
Sign on to:   
Receive email
updates
  
My Account
authorized users
  
Edit Profile   
 
Help   
About T-Space   

T-Space at The University of Toronto Libraries >
School of Graduate Studies - Theses >
Master >

Please use this identifier to cite or link to this item: http://hdl.handle.net/1807/25797

Title: Decarburization and Melting Behavior of Direct-reduced Iron Pellets in Steelmaking Slag
Authors: Sharifi Kiasaraei, Erfan
Advisor: Barati, Mansoor
Department: Materials Science and Engineering
Keywords: Steelmaking
DRI
Issue Date: 11-Jan-2011
Abstract: An experimental study was undertaken to quantify the rate of DRI decarburization in a steelmaking slag using the constant–volume pressure increase technique. Experiments were conducted by dropping DRI pellets into molten slag at temperatures from 1500°C to 1600°C. Further experiments were carried out in which the DRI pellets were preheated while the slag temperature remained constant. The effect of initial carbon content and preheating temperature of the DRI on the reaction rate was investigated. The decarburization of DRI appears to comprise of two stages; reaction with the FeO of DRI, followed by further decarburization through the iron oxide of slag. Carbon has a significant effect on the kinetics of both stages while the preheating temperature mainly influences the rate of the reaction between FeO and carbon inside the pellet.
URI: http://hdl.handle.net/1807/25797
Appears in Collections:Master

Files in This Item:

File Description SizeFormat
SharifiKiasaraei_Erfan_201011_MAS_thesis.pdf3.07 MBAdobe PDF
View/Open

This item is licensed under a Creative Commons License
Creative Commons

Items in T-Space are protected by copyright, with all rights reserved, unless otherwise indicated.

uoft